科润Thinkre®系列全氟醚橡胶可以制备用于耐高温、耐化学品腐蚀、耐辐射、耐大气老化等场合的垫片、O型圈、V型密封件、骨架油封、隔膜、胶管、电缆护套、隔热布、阀片、伸缩接头、胶辊、涂层等产品。该系列拥有优异的耐高温性能和耐化学溶剂性能，同时具有低渗透率，优异的耐等离子体刻蚀性能, 可靠性及长效使用寿命。
聚合物原料基本参数
| 产品参数Specifications |
FFKM3000-150 |
FFKM3000-110 |
FFKM3000-80 |
FFKM3000-50 |
Test Method |
门尼粘度ML(1+10min)@121℃
Mooney Viscosity(MU) |
145±15 |
115±15 |
85±15 |
55±15 |
ASTM D1646 |
| 比重 Specific Gravity(g/cm³) |
2.02±0.03 |
2.02±0.03 |
2.02±0.03 |
2.02±0.03 |
ASTM D792 |
| 外观 Appearance |
白色半透明 Translucent White |
目测
visual inspection |
包装储存和安全注意事项 Packing, Storage and Safety
该产品应储存于阴凉、通风的库房；避免潮湿环境或阳光直射；远离火种、热源，常温储存。保持包装密封。
应采取正常护理和预防措施以避免接触物品时损伤皮肤、眼睛；避免吸入气味。
不同混炼配方下的测试结果对比
| 性能指标Proper |
Property |
单位
Unit |
测试结果Test Value |
测试标准
Test Method |
| 混炼配方Formulation |
| 测试配方Standard Formulation |
|
1 |
2 |
3 |
4 |
|
| 样品编号 |
Sample Number |
|
FFKM3000-150 |
FFKM3000-110 |
FFKM3000-80 |
FFKM3000-50 |
|
| 聚合物原料 |
Raw Polymer |
phr |
100 |
100 |
100 |
100 |
- |
| BOAP |
(*CAS#83558-87-6) |
phr |
1.2 |
1.2 |
1.2 |
1.2 |
- |
| N-990 MT Carbon Black |
phr |
20 |
20 |
20 |
20 |
- |
| 无转子硫化仪测试 MDR:60min @170℃ and Arc0.5° |
| 最小扭矩 |
Minimum Torque |
lb-in |
4.2 |
3.2 |
2.7 |
1.3 |
ASTM D2084 |
| 最大扭矩 |
Maximum Torque |
Ib-in |
16.4 |
16.0 |
15.2 |
12.5 |
ASTM D2084 |
| ts2 |
|
min |
4.3 |
4.2 |
4.7 |
5.4 |
ASTM D2084 |
| t'50 |
|
min |
10.5 |
8.8 |
9.1 |
9.0 |
ASTM D2084 |
| t'90 |
|
min |
22.7 |
21.9 |
23.7 |
19.5 |
ASTM D2084 |
| 加压硫化Press Cure:30min @170℃,Post Cure:(8+16)h @290℃ |
| 100%模量 |
100% Modulus |
MPa |
18.3 |
16.8 |
14.9 |
11.6 |
ASTM D412C |
| 拉伸强度 |
Tensile Strength |
MPa |
22.9 |
20.9 |
20.7 |
17.9 |
ASTM D412C |
| 断裂伸长率 |
Elongation @Break |
% |
120.5 |
119.3 |
127.5 |
142.7 |
ASTM D412C |
| 硬度 |
Hardness |
ShoreA |
81 |
77 |
77 |
72 |
ASTM D2240 |
| 热老化Heat Aging,70h@300℃ |
| 硬度变化 |
△Hardness |
ShoreA |
-4 |
-3 |
-3 |
-3 |
ASTM D573 |
| 拉伸强度变化 |
△Tensile Strength |
|
-13% |
-8% |
-12% |
-13% |
ASTM D573 |
| 断裂伸长率变化 |
△Elongation @Break |
|
11% |
14% |
17% |
16% |
ASTM D573 |
| 质量变化 |
△Weight |
|
-0.7% |
-0.7% |
-0.9% |
-0.9% |
ASTM D573 |
| 压缩永久变形Compression Set:15%Deformation |
| 70h @300℃ |
% |
24 |
25 |
27 |
27 |
ISO815
6.3mm molded |